SrTiO₃(001)表面

不同吸附位置

原子间距 (Å)

(between N and #)

(eV)

是否弛豫优化

E(N₂)

E(N)

TiO2原子层截止

O_s(I)

1.33 (#: O_s(I))

1.33

2.39

Yes

Ti_s(I)

1.92 (#: Ti_s(I))

0.39

1.25

Yes

Interstice A

0.25 (#: A)

1.62

2.67

Yes

SrO原子层截止

O_s(1)

1.35 (#: O_s(1))

0.97

1.93

Yes

Sr_s(1)

2.46 (#: Sr_s(1))

0.15

0.74

Yes

Interstice B

0.94 (#: B)

1.24

2.16

Yes