熔盐电解质体系 | 实验温度(K) | 密度(g/cm3) | 粘度(mPa·s) |
Na3AlF6 + 3LiFwt.% | 1300 | 2.065 (2.071a) | - |
1250 | 2.107 (2.113a) | - | |
Na3AlF6 + 7.6LiFwt.% | 1300 | 2.049 (2.053a) | - |
1250 | 2.062 (2.093a) | - | |
Na3AlF6 + 15.7LiFwt.% | 1300 | 2.038 (2.028a) | - |
1250 | 2.053 (2.073a) | - | |
Na3AlF6 + 12.6LiFwt.% | 1300 | - | 1.16 (1.09a) |
Na3AlF6 + 27.8LiFwt.% | 1300 | - | 0.94 (0.89a) |
KR0.1 + 22wt.%AlF3 | 1193 | 1.967 (1.981b) | - |
1213 | 1.951 (1.952b) | - | |
1233 | 1.934 (1.927b) | - | |
KR0.2 + 22wt.% | 1193 | 1.970 (1.973b) | - |
1213 | 1.953 (1.955b) | - | |
1233 | 1.937 (1.938b) | - |