| Expt. | Other calculations | Present |
Fe | D/(10−9 m2×s−1) |
| 5.7 [19] , 6.0 [20] (251 GPa, 6000 K) | 5.85 (250 GPa, 6000 K) |
η/(mPa×s) |
| 8 ± 3 [20] (251 GPa, 6000 K) 6.65 ± 0.3 [21] (141 GPa, 5000 K) | 10.91 (250 GPa, 6000 K) 7.02 (150 GPa, 5000 K) | |
Mo | η/(mPa×s) | 5.0 ± 0.5 [22] [23] (0 GPa, 2896 K) |
| 7.70 (0GPa, 2900 K) |
Eη/(eV) | 0.586 [22] , 0.757 [23] (0 GPa) |
| 0.567 (0 GPa) | |
Ta | η/(mPa×s) | 8.8 [23] , 8.5 [24] (0 GPa, 3293 K) |
| 7.07 (0GPa, 3300K) |
Eη/(eV) | 0.815 [24] , 2.211 [23] (0 GPa) |
| 0.564 (0 GPa) | |
W | η/(mPa×s) | 8.5 ± 0.9 [23] (0 GPa, 3695 K) |
| 11.19 (0 GPa, 4230 K) |
Eη/(eV) | 1.26 ± 0.25 [23] (0 GPa) |
| 0.758 | |
Ni | D/(10−9 m2×s−1) | 3.8 [25] (0 GPa, 1795 K) | 4.4 [26] (0 GPa, 1850 K) | 3.54 (0 GPa, 1443 K) |
η/(mPa×s) |
| 3.6-5.5 [26] (0 GPa) | 3.18 (0 GPa, 1501 K) | |
Cu | D/(10−9 m2×s−1) | 5.2 [27] (0 GPa, 1620 K) 4.85 [27] (0 GPa, 1570 K) |
| 5.12 (0 GPa, 1600 K) |
η/(mPa×s) | 4.03 [28] (0 GPa, 1356 K) | 4.07 [1] , 4.20 [1] (0 GPa, 1356 K) | 4.16 (0 GPa, 1300 K) | |
ED/(eV) | 0.337 [27] (0 GPa) |
| 0.382 (0 GPa) |