试件编号 | 开裂状态 | 峰值状态 | 破坏状态 |
| 破坏转角 | |||
Vcr/kN | Δcr/mm | Vu/kN | Δu/mm | Vd/kN | Δd/mm | |||
W1 | −180.3 | 1.1 | +297.4 | +4.0 | +252.8 | +6.1 | 1.44 | 1/248 |
−223.3 | −3.7 | −189.8 | −6.0 | |||||
SW2 | +203.7 | +2.9 | +452.5 | +13.7 | +384.6 | +19.7 | 1.99 | 1/69 |
−360.1 | −20.9 | −306.1 | −24.4 | |||||
ZW1 | −191.7 | −1.3 | +237.3 | +2.9 | +201.7 | +7.7 | 1.22 | 1/176 |
−231.0 | −5.7 | −196.4 | −9.6 | |||||
SZW2 | +218.3 | +2.2 | +342.2 | +10.4 | +290.9 | +19.2 | 1.48 | 1/75 |
−301.9 | −12.0 | −256.6 | −20.6 | |||||
DW1 | −183.5 | −1.1 | +223.9 | +2.4 | +190.3 | +6.0 | 1.18 | 1/263 |
−209.2 | −2.9 | −177.8 | −5.4 | |||||
SDW2 | −203.9 | +1.9 | +271.6 | +5.4 | +230.9 | +10.5 | 1.31 | 1/143 |
−261.0 | −6.9 | −221.9 | −10.5 |