温度(℃) | 密度(g/cm3) | 杨氏模量(Pa) | 泊松比 | 比热(J/kg K) | 热导率(W/mK) | 膨胀系数(m/K) |
25 | 1.78683 | 4.62E+10 | 0.29214 | 1.01E+03 | 82.33476 | 2.49E−05 |
100 | 1.77663 | 4.45E+10 | 0.29736 | 1.05E+03 | 87.01007 | 2.55E−05 |
200 | 1.76237 | 4.19E+10 | 0.30434 | 1.10E+03 | 93.14288 | 2.64E−05 |
300 | 1.74739 | 3.89E+10 | 0.31137 | 1.14E+03 | 99.21667 | 2.74E−05 |
400 | 1.73174 | 3.56E+10 | 0.31843 | 1.18E+03 | 105.25875 | 2.83E−05 |
500 | 1.71494 | 3.11E+10 | 0.32654 | 2.54E+03 | 111.30089 | 2.94E−05 |
600 | 1.66912 | 2.06E+09 | 0.41178 | 6.64E+03 | 99.4966 | 4.09E−05 |
700 | 1.61289 | 9.75E−04 | 0.49991 | 1.40E+03 | 79.93853 | 5.33E−05 |
800 | 1.58666 | 4.09E−05 | 0.49996 | 1.40E+03 | 86.71718 | 5.43E−05 |