| 材料 | 加工方法 | 降解实验结果 | 力学实验结果 | 参考文献 |
| Zn | 热挤压 | Ecorr—−0.098 V Icorr—8.9 µA/cm2 DR—0.133 mm/y | δTYS—55 MPa δUTS—97 MPa | [86] |
| Zn | 热轧 | Ecorr—−1.077 V Icorr—20.9 µA/cm2 DR—0.306 mm/y | δTYS—35 MPa δUTS—49 MPa | [87] |
| Zn-25Mg | 粉末冶金 | Ecorr—−1.323 V Icorr—12.2 µA/cm2 DR—0.373 mm/y | E—86 MPa δcys—403 MPa | [74] |
| Zn-1.3Fe | 铸造 | Ecorr—−1.02 V Icorr—0.67 µA/cm2 DR—0.01 mm/y | δTYS—80 MPa δUTS—134 MPa | [88] |
| Zn-3Cu-1Fe | 挤压 | Icorr—8.9 µA/cm2 DR—0.13 mm/y | δTYS—272 MPa δUTS—221 MPa | [89] |
| Zn-0.5Al-0.5Mg-0.3Bi | 挤压 | Ecorr—−1.084 V Icorr—16.45 µA/cm2 DR—0.203 mm/y | δUTS—108 MPa H—44.75 HV | [90] |