2θ

D

D_o

h k l

I%

2θ

D

D₀

h k l

I%

8.380

10.556

10.542

0 1-1

9

33.760

2.651

2.652

0-4-2

37

9.320

9.046

9.036

1 0-1

5

35.060

2.558

2.557

0-3-5

19

9.780

9.483

9.481

1 0 0

8

36.300

2.468

2.472

3-2-5

4

11.660

7.564

7.583

1-1-1

9

37.200

2.419

2.418

1 4 2

4

12.040

7.341

7.344

1 0-2

13

38.600

2.329

2.330

1-5 2

6

14.300

6.187

6.188

1-1 2

9

39.220

2.297

2.295

2 4-2

7

16.460

5.395

5.381

1-2 0

5

40.500

2.227

2.225

4 1-3

5

17.300

5.132

5.121

1-2-1

4

41.100

2.192

2.194

4-3 1

4

19.280

4.595

4.599

1 2-1

100

41.980

2.150

2.150

1 3 6

13

19.980

4.420

4.440

1 2-2

9

42.540

2.121

2.123

1-4 7

5

20.960

4.227

4.234

1-1-4

10

43.460

2.079

2.080

4 2-1

7

21.320

4.165

4.164

2 1-1

65

44.060

2.053

2.053

3-5 1

13

21.660

4.106

4.099

2 1 0

9

44.580

2.029

2.030

2 4 3

4

23.480

3.782

3.785

2-2-2

26

45.140

2.004

2.006

1-5 6

8

24.280

3.662

3.662

1 2-4

27

46.600

1.946

1.947

2 5-1

8

25.040

3.550

3.553

0-1-5

6

48.020

1.895

1.893

1-5 7

13

26.580

3.345

3.350

2 2 0

5

48.520

1.872

1.874

0 4 7

8

27.400

3.250

3.252

2-3-1

15

49.480

1.842

1.840

3 4 2

4

28.340

3.151

3.146

3-1-2

11

50.920

1.788

1.791

1-5 8

8

28.940

3.089

3.082

1-2-5

16

52.720

1.734

1.734

3 1 8

5

29.340

3.036

3.041

0 2 5

11

53.640

1.772

1.772

1 6 1

6

29.760

3.008

3.011

3-1-3

10

56.180

1.637

1.635

0 7 0

7

30.200

2.955

2.956

1 0 6

12

60.420

1.530

1.530

2 4 8

10

30.640

2.916

2.915

1-4 1

10

63.64

1.462

1.460

2 7 0

4

31.100

2.865

2.873

0 4 0

44

67.580

1.387

1.385

0 7 6

4

31.820

2.807

2.810

3 1 1

5

71.000

1.325

1.326

0 8 4

4

33.000

2.712

2.712

1-4-2

4