催化剂组成 | 反应温度/℃ | 原料组成 | 催化剂质量/g | 丙烷转化率/% | 丙烯选择性/% | 文献 | |
Cr2O3/SiO2 | 550 | C3H8:CO2 = 1:7 | 0.5 | 29.7 | 80.5 | [29] | |
yCrOx/silicalite-1(y = 3) | 550 | C3H8:CO2:Ar = 4:20:1 | 0.5 | 45 | 65 | [28] | |
Ga2O3/TiO2 | 600 | C3H8:CO2:N2 = 1:2:15 | 0.2 | 9 | - | [34] | |
Ga2O3/Al2O3 | 600 | C3H8:CO2:N2 = 1:2:15 | 0.2 | 23 | - | [34] | |
Ga2O3/ZrO2 | 600 | C3H8:CO2:N2 = 1:2:15 | 0.2 | 18 | - | [34] | |
Ga2O3/Al2O3 | 550 | C3H8:CO2:N2 = 1:3:27 | 0.15 | 35.35 | 95 | [35] | |
Ga2O3/SiO2 | 600 | C3H8:CO2:N2 = 1:3:10 | 1 | 30~45 | 90-92 | [36] | |
Rh/Al2O3 | 550 | C3H8:CO2 = 1:3 | 0.3 | 7 | 25 | [37] | |
5%Ru/CeO2 | 550 | C3H8:CO2:Ar = 1:2:5 | 0.25 | 3.7 (m2/g) | - | [38] | |
5%Ru/ZrO2 | 550 | C3H8:CO2:Ar = 1:2:5 | 0.25 | 2.5 (m2/g) | - | [38] | |
CeZrAlOx | 500 | C3H8:CO2:He = 4:4:3 | 0.2 | 3 | 82 | [39] | |
5%Pd/CeZrAlOx | 500 | C3H8:CO2:He = 4:4:3 | 0.2 | 3.3 | 76 | [39] | |
5%Pd/CeZrOx | 500 | C3H8:CO2:He = 4:4:3 | 0.2 | 10.1 | 92 | [39] | |
0.05%Pt/Al2O3 | 575 | - | 0.1 | 5 | 95 | [40] | |
5%Pt/Al2O3 | 575 | - | 0.1 | 27 | 62 | [40] | |
Fe3Ni/CeO2 | 550 | C3H8:CO2:Ar = 1:1:2 | 0.1 | 2.7 | 58.2 | [41] | |
Fe3Pt/CeO2 | 550 | C3H8:CO2:Ar = 1:1:2 | 0.1 | 1.1 | 32 | [41] | |
Ni3Pt/CeO2 | 550 | C3H8:CO2:Ar = 1:1:2 | 0.1 | 11.6 | 2.8 | [41] | |
Pt1Fe5/S-1 | 550 | C3H8:CO2:N2 = 1:1:6 | 0.15 | 43 | 92 | [42] | |
PtCo/SiBeta | 550 | C3H8:CO2:N2 = 1:1:3 | 0.1 | 51.8 | 92 | [43] | |
0.1 wt%Pt/1.0 wt%Sn/CeO2 | 550 | - | 0.15 | 15.1 | 63.9 | [44] | |
1Pt/1Sn-CeO2 | 550 | C3H8:CO2:Ar = 1:2:4 | 1 | 64 | 18 | [45] | |
1Pt/CeO2 | 500 | C3H8:CO2:N2 = 4:1:20 | 0.5 | 42 | 19 | [46] | |
1Pt7Sn/CeO2 | 500 | C3H8:CO2:N2 = 4:1:20 | 0.5 | 18 | 80 | [46] | |
PtSn/SiO2 | 550 | C3H8:CO2 = 1:1 | 0.2 | 50 | 93 | [47] | |
PtSn3/SiO2 | 550 | C3H8:CO2 = 1:1 | 0.2 | 47 | 96 | [47] | |
Pt-Co-In/CeO2 | 550 | C3H8:CO2:He = 1:1:2 | 0.2 | 47~52 | 95~99 | [12] |