| 试验条件 | 试验结果 | |||||||||||
序号 | T (℃) | T (h) | 包覆量% | TD (g/cm3) | BET (cm2/g) | D10 (um) | D50 (um) | D90 (um) | D99.99 (um) | pH | 0.5 C容量(mAh/g) | 1.0 C容量(mAh/g) | 50次容量保持率(%) |
1 | 750 | 10 | 0 | 2.72 | 0.412 | 8.41 | 13.06 | 20.39 | 42.8 | 11.42 | 158.2 | 157 | 95.50% |
2 | 750 | 10 | 0.2 | 2.76 | 0.353 | 8.48 | 13.55 | 21.27 | 44.24 | 11.42 | 157.7 | 156.5 | 97.82% |
3 | 750 | 10 | 0.3 | 2.8 | 0.295 | 8.51 | 13.59 | 21.45 | 44.38 | 11.35 | 157.5 | 156.2 | 99.05% |
4 | 750 | 10 | 0.5 | 2.83 | 0.278 | 8.88 | 13.67 | 25.55 | 57.45 | 11.33 | 156 | 155.6 | 99.01% |
5 | 750 | 8 | 0.3 | 2.7 | 0.345 | 8.43 | 13.21 | 20.42 | 44.95 | 11.52 | 157.7 | 156.6 | 97.05% |
6 | 750 | 14 | 0.3 | 2.91 | 0.212 | 9.55 | 15.68 | 28.31 | 58.86 | 11.25 | 153.1 | 151.2 | 99.02% |
7 | 700 | 10 | 0.3 | 2.65 | 0.401 | 8.43 | 13.25 | 20.45 | 44.98 | 11.55 | 157.8 | 156.5 | 96.62% |
8 | 800 | 10 | 0.3 | 2.95 | 0.204 | 9.58 | 15.84 | 28.77 | 60.45 | 11.27 | 152.2 | 151.2 | 99.10% |
验证试验 | 750 | 10 | 0.3 | 2.81 | 0.293 | 8.52 | 13.6 | 21.54 | 44.52 | 11.33 | 157.7 | 156.3 | 99.03% |