试验号 | Al2O3 | ZrO2 | MgO | 断裂韧性 KIC/MPa∙m1/2 | HV/GPa | 耐腐蚀性 |
0 | 0 | 0 | 0 | 3.86 | 16.22 | 较差(ULC) |
1 | 5% | 5% | 5% | 4.65 | 15.12 | 较好(ULA) |
2 | 5% | 3% | 3% | 4.55 | 15.36 | 较好(ULA) |
3 | 5% | 1% | 1% | 4.02 | 15.59 | 一般(ULB) |
4 | 3% | 5% | 3% | 5.27 | 13.22 | 最佳(ULA) |
5 | 3% | 3% | 1% | 4.79 | 14.93 | 一般(ULA) |
6 | 3% | 1% | 5% | 4.01 | 15.25 | 较差(ULB) |
7 | 1% | 5% | 1% | 4.43 | 15.01 | 一般(ULA) |
8 | 1% | 3% | 5% | 4.39 | 15.66 | 一般(ULA) |
9 | 1% | 1% | 3% | 3.99 | 15.98 | 较差(ULC) |