序号 | 实验条件 | 比表面积 (m2/g) | 单点吸附 总孔容(cm3/g) | 吸附平均孔径(nm) | 微孔容HK法 (m3/g) | 最可几孔径 HK法(nm) | 中值孔径 HK法(nm) |
1 | 500℃预处理&900℃&CO2气氛5 h | 1226 | 0.920 | 3.001 | 0.4885 | 0.7718 | 0.8571 |
2 | 600℃预处理&900℃&CO2气氛 5 h | 1288 | 0.535 | 1.662 | 0.5039 | 0.6338 | 0.7567 |
3 | 500℃预处理&碱炭比1:2 &900℃ 1 h | 779 | 0.333 | 1.712 | 0.3078 | 0.6075 | 0.7260 |
4 | 600℃预处理&碱炭比1:2 &900℃ 1 h | 1723 | 0.755 | 1.752 | 0.6752 | 0.7726 | 0.8025 |
5 | 700℃预处理&碱炭比1:2 &900℃ 1 h | 718 | 0.335 | 1.868 | 0.2840 | 0.6120 | 0.7448 |
6 | 800℃预处理&碱炭比1:2 &900℃ 1 h | 650 | 0.303 | 1.862 | 0.2653 | 0.6545 | 0.7690 |
7 | 500℃预处理&碱炭比2:1&900℃ 1 h | 750 | 0.344 | 1.835 | 0.2960 | 0.6667 | 0.7376 |
8 | 600℃预处理&碱炭比2:1&900℃ 1 h | 1911 | 0.855 | 1.789 | 0.7507 | 0.7720 | 0.8080 |
9 | 700℃预处理&碱炭比2:1&800℃ 1 h | 1859 | 0.765 | 1.646 | 0.7251 | 0.7757 | 0.7943 |
10 | 800℃预处理&碱炭比2:1&800℃ 1 h | 942 | 0.378 | 1.603 | 0.3696 | 0.6785 | 0.7184 |
11 | 炭化料 碱炭比2:1&900℃ 1 h | 984 | 0.430 | 1.747 | 0.3864 | 0.5978 | 0.7486 |
12 | 400℃预处理&碱炭比2:1&850℃ 1 h | 2074 | 0.926 | 1.748 | 0.8425 | 0.8012 | 0.8169 |
13 | 500℃预处理&碱炭比2:1&850℃ 1 h | 1830 | 0.778 | 1.699 | 0.7160 | 0.7719 | 0.7922 |
14 | <1 mm炭化料 碱炭比2:1&850℃ 1 h | 1992 | 0.842 | 1.690 | 0.7803 | 0.7708 | 0.7956 |
15 | 3 mm炭化料 碱炭比2:1&850℃ 1 h | 1784 | 0.784 | 1.758 | 0.6999 | 0.6370 | 0.7853 |