孪晶界间距 | 屈服应变(%) | 屈服强度(Gpa) |
λ= 0.67 nm | 0.054 | 2.864 |
λ= 1.55 nm | 0.054 | 2.997 |
λ= 2.43 nm | 0.055 | 3.037 |
λ= 3.31 nm | 0.054 | 2.826 |
λ = 4.19 nm | 0.053 | 2.706 |